|Recommended Dosage:||1%-5%||Colour:||White Or Grey|
|Melting (℃):||130℃～140℃||MFI:||≥1.5 G/10min|
|Grade:||Industrial||Ingredient:||PE, CaO, CaCO3|
|Texture:||Plastic||Application Process:||Injection Molding, Blowing Film, Extrusion, Etc.|
|Form:||Granular||Water Absorption:||20% Of Self-weight|
anti corrosion masterbatch
PE Synthetic Resin Calcium Oxide Cao Desiccant Masterbatch For Recycled Plastic
Our desiccant masterbatch is designed specifically for removing moisture from recycled PE/PP during processing. Its great advantage is it can effectively absorb moisture while processing, so that the recycled PE/PP scraps and granule could be directly used to make plastic products without pre-drying.And the product quality could be proved to be very good.
Desiccant Masterbatch is used in recycled plastic production such as Film blowing, injection molding, etc.
1. High effectiveness humidity absorbing on market.
2. Low dosage -keep better mechanical properties
3. Unform micro particle diameter, no joint particles
4. Long valid time of outside package
5. No mesh-clogging
|Colour||White or grey|
|Application process||Injection molding, blowing film, extrusion, etc.|
|Suitable for||PE or PP|
|Ingredient||PE, CaO, CaCO3|
|Valid time||12~48 hours after bags open|
|Water absorption||20% of self-weight|
|Function||Eliminate the moisture in plastic raw materials|
|Active ingredient||50-80% or more|
When the defoaming masterbatch is stirred with the moisture-affected plastic material directly, the product can be processed and produced. For example, the proportion of defoaming masterbatch added is 1%-2% for blown film production. If used in sheet and injection moulding production, the addition ratio is 2%-5%. If used in pipe production, add 2%-5%. Specific addition proportion should be added at the discretion of users according to the moisture condition of plastics.